The effect of heat treatment on microstructure and wear behavior of TC21 (Ti-6Al-2Sn-2Zr-3Mo-1Cr-2Nb-Si, wt.%) Ti-alloy was investigated. The samples were solution treated at 900°C for 15 min followed by furnace cooling to 800°C with a cooling rate 1°C/min and holding for 20 min, then the samples cooled down to room temperature either using water quenching (WQ) or air cooling (AC). Consequently, aging treatment was applied at 575°C for 4 hr. The microstructure feature showed a secondary α phase (αRsR) precipitated in residual β phase due to the step cooling from 900°C to 800°C inside furnace as well as the aging treatment. The highest wear rate was obtained for WQ samples due to increasing in volume fraction of αRp R(58%). However, the lowest wear rate was reported for WQ +Aging samples due to the high hardness.