Metal rolling processes are usually subjected to continuous development for increasing the
efficiency of metals industry and broadening the applicability of soft metals in the structural
applications. During this study, cold plate rolling have been conducted under different
conditions. Particularly, the rolling power and the resulted separating force have been
analyzed after changing the roll diameter, the draft thickness, and the lubricant type. It was
observed that, decreasing the reduction by pass and reducing the roll diameter could minimize
the need for high power during operation. It was also noticed that, among the different
experiments, using olive and paraffin oil as lubricant at the roll-metal surface show a
significant effect on reducing the power consumption and increasing the rolling process
efficiency in a high agreement with the mathematical modeling.
 
تعتبر دراسة قوي الفصل من أھم العناصر إثناء عملية الدرفلة.فيھتم ھذا البحث بدراسة قوي الفصل إثناء الدرفلة علي البارد
لشيتات من الالومنيوم..حيث أنھا عامل رئيسي للطاقة المستھلکة إثناء عمليھ الدرفلة.وان ھذه القوي تتأثر بعوامل عديدة منھا
المادة المراد عمل درفلھ لھا وقطر الدرفيل المستخدم ونسبھ التخفيض إثناء عملية الدرفلة وسمک المادة إثناء الدخول
ومعامل الاحتکاک بين الدرفيل والمادة والسرعة النسبية بين الدرفيل والمادة ونوع عملية الدرفلة. فالزيادة في قطر الدرفيل
ونسبة التخفيضومعامل الاحتکاک يؤدي الي زيادة قوي الفصل. ويمکن التغلب علي بعضالعناصر مثل الاحتکاک باستخدام
نوع تزييت مناسب وبالتالي نقلل قوي الفصل ونحافظ علي سطح الدرفيل.وقد تبين أيضا من البحث عند دراسة العلاقة بين
الطاقة المستھلکة والزمن ان الطاقة تصل إلي أقصي قيمھ في البداية ثم تنخفضوتستمر لوقت معين لإنھاء عمليھ الدرفلة ثم
تقل الي اقل قيمھ بعد انتھاء عملية الدرفلة .